Advancements in Dental Care: The Evolving Landscape of Prosthetic Dentistry.

In the dental field, the specialty of prosthodontics stands out as the frontline of innovation, continually pushing the boundaries to enhance both function and aesthetics for optimal oral rehabilitation [...].

Characterization of Microstructure, Optical Properties, and Mechanical Behavior of a Temporary 3D Printing Resin: Impact of Post-Curing Time.

The present study aimed to characterize the microstructure of a temporary 3D printing polymer-based composite material (Resilab Temp), evaluating its optical properties and mechanical behavior according to different post-curing times. For the analysis of the surface microstructure and establishment of the best printing pattern, samples in bar format following ISO 4049 (25 × 10 × 3 mm) were designed in CAD software (Rhinoceros 6.0), printed on a W3D printer (Wilcos), and light-cured in Anycubic Photon for different lengths of time (no post-curing, 16 min, 32 min, and 60 min). For the structural characterization, analyses were carried out using Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM). The mechanical behavior of this polymer-based composite material was determined based on flexural strength tests and Knoop microhardness. Color and translucency analysis were performed using a spectrophotometer (VITA Easy Shade Advanced 4.0), which was then evaluated in CIELab, using gray, black, and white backgrounds. All analyses were performed immediately after making the samples and repeated after thermal aging over two thousand cycles (5-55 °C). The results obtained were statistically analyzed with a significance level of 5%. FT-IR analysis showed about a 46% degree of conversion on the surface and 37% in the center of the resin sample. The flexural strength was higher for the groups polymerized for 32 min and 1 h, while the Knoop microhardness did not show a statistical difference between the groups. Color and translucency analysis also did not show statistical differences between groups. According to all of the analyses carried out in this study, for the evaluated material, a post-polymerization time of 1 h should be suggested to improve the mechanical performance of 3D-printed devices.

Can the Remaining Coronal Tooth Structure Influence the Mechanical Behavior of Nonpost Full Crowns?

OBJECTIVES: This study investigated the impact of the remaining coronal tooth structure on the mechanical behavior of nonpost (NP) full crowns on endodontically treated maxillary central incisors. MATERIALS AND METHODS: Forty bovine incisors with NP and 2-mm of ferrule were divided into four groups based on the remaining structure: complete 2-mm ferrule (NP-2), absence of mesial and distal ferrule effect (NP-BL), absence of buccal and lingual ferrule effect (NP-MD), and no ferrule (NP-0). The specimens underwent a stepwise stress fatigue test until fracture occurred, and stress distribution was analyzed using in silico finite element analysis (FEA). Additionally, groups with endodontic posts (P) were simulated in the FEA. RESULTS: The results showed that the survival rates varied among the different groups under oblique loading. The NP-2 group exhibited the highest survival rate, with all samples enduring loads up to 200 N and some surviving up to 520 N. The NP-MD and NP-BL groups had lower survival rates, while the NP-0 group had the poorest survival rate. The predominant failure mode was a nonrepairable root fracture. FEA results indicated no significant difference between groups with and without posts. NP intraradicular restorations on nonweakened roots with a minimum height of 2mm and partial or total ferrule thickness of 1mm offer a promising treatment option. CONCLUSION: A complete 2-mm ferrule was found to be the most favorable configuration for NP full crowns. However, maintaining the remaining tissue is crucial, as both combinations with preserved ferrule effect exhibited superior behavior in terms of fatigue and fracture load compared to the group with no ferrule. These findings contribute to understanding the mechanical considerations for NP full crowns and provide insights into treatment planning and design choices in restorative dentistry.

Influence of CAD-CAM milling strategies on the outcome of indirect restorations: A scoping review.

STATEMENT OF PROBLEM: The influence of computer-aided manufacturing (CAM) parameters and settings on the outcomes of milled indirect restorations is poorly understood. PURPOSE: The purpose of this scoping review was to summarize the current CAM systems, parameters, and setting changes, and their effects on different outcomes of milled indirect restorations and aspects related to their manufacture. MATERIAL AND METHODS: The protocol of this review is available online (https://osf.io/x28ps/). Studies that used at least 2 different parameters (CAM units, number of axes, digital spacers, or protocols with different rotatory instruments, grit-sizes, milling speed, or others) for milling indirect restorations were included. A structured search up to July 2023 was performed by 2 independent reviewers for articles written in English in LILACS, MEDLINE via PubMed, EMBASE, Web of Science, and Scopus. RESULTS: Of 1546 studies identified, 22 were included in the review. Discrepancies were found between the planned and actual measured cement space, with a decreasing linear relationship impacting restoration adaptation at different points. The CEREC MC XL milling machine was the most used system in the included studies, with variations in bur types, milling modes, and number of burs uses affecting internal fit and surface trueness. The results demonstrated the better adaptation of restorations made with 5-axis over 3-axis milling machines. Lithium disilicate and zirconia were the most commonly used materials, and crowns and inlays were popular designs. Marginal and internal adaptation were the primary outcomes assessed using the various techniques. CONCLUSIONS: The study presented a comprehensive exploration of CAM systems and parameters, and their influence on indirect restorations. The planned cement space was not properly reproduced by the milling. Bur characteristics can affect restoration fit and trueness. The 5-axis units seem to result in better-adapted restorations compared with 3- and 4-axis units.

Enhancing mouthguard longevity: Impact of surface treatment against aging from brushing and disinfectant exposure.

BACKGROUND/AIMS: The study aimed to assess the surface characteristics of sports mouthguards under mechanical stresses during cleaning, either by brushing or immersion in disinfectant solutions. MATERIAL AND METHODS: Ethylene-vinyl acetate samples, 4 mm thick, were randomly assigned to cleaning methods: control (C-no cleaning), brushing with water (B.W), brushing with neutral liquid soap (B.S), brushing with toothpaste (B.T), immersion in distilled water for 10 min (I.W), immersion in 2.25% sodium hypochlorite solution for 10 min (I.SH), and immersion in sodium bicarbonate solution for 5 min (I.SB). All cleaning methods were applied for 28 days. Surface roughness average (Ra) and wettability were measured at baseline for the control group (n = 9), and after cleaning for all the other groups. RESULTS: One-way ANOVA with Tukey tests (5% significance) indicated significant differences among groups (p < .05). The I.SB group had higher surface roughness than B.S and B.T (p < .05). B.W showed the lowest wettability, significantly lower than B.T, I.W, and I.SB (p < .05). I.SB exhibited the highest wettability, significantly different from sodium hypochlorite, neutral liquid soap, brushing with water, and control groups (p < .05). The sodium bicarbonate immersion group (I.SB) demonstrated greater statistical variation, displaying higher susceptibility to aging compared to brushing with neutral liquid soap. CONCLUSION: Cleaning mouthguards with a toothbrush, water, and neutral liquid soap emerged as the most promising method, causing minimal surface changes in the material.

Effect of brushing simulation on the wear behavior of repaired CAD-CAM restorations.

OBJECTIVE: The aim of the present study was to evaluate the influence of multidirectional brushing on the surface roughness, morphology, and bonding interface of resin-repaired CAD-CAM ceramic and composite restorations. MATERIALS AND METHODS: Twelve (N = 12) blocks (4 mm × 4 mm × 2 mm for parallel axis; 5 mm × 4 mm × 2 mm for perpendicular axis) of lithium disilicate glass-ceramic (IPS e.max CAD, Ivoclar AG) and CAD-CAM resin composite (Tetric CAD, Ivoclar AG) were obtained and repaired with direct resin composite (Clearfil AP-X, Kuraray). An abrasive slurry was prepared and the brushing was performed according to each restorative material and axis of brushing (n = 6; perpendicular to repair interface and parallel to repair interface) during 3,650 cycles (240 strokes per minute) to simulate 3 years of brushing. The surface roughness (Ra) and the profile variation for each material (restoration and direct repair resin composite) were measured at the baseline condition and after brushing, and the mean roughness and presence of steps at the repair interface were evaluated through factorial analysis of Variance (ANOVA). Scanning Electron Microscopy (SEM) images were taken to evaluate the surface topography of the repaired materials after brushing. RESULTS: The mean roughness of the repaired CAD-CAM restorations was affected by the brushing (P < .05), mainly when evaluating the repair material and the interface (P < .05), while the restorative CAD-CAM materials presented more stable values. The profile evaluation showed higher steps at the interface when repairing lithium disilicate than for CAD-CAM resin composite. CONCLUSION: Repaired CAD-CAM restorations were susceptible to wear after brushing simulation. The surface roughness of the direct resin composite was the most affected leading to step development at the interface, particularly in the repaired lithium disilicate samples. Cinical maintenance recalls and polishing protocols must be considered to enhance the longevity of such restorations.

Repair protocols for indirect monolithic restorations: a literature review.

Despite the advancements in indirect monolithic restorations, technical complications may occur during function. To overcome this issues, intraoral repair using resin composite is a practical and low-cost procedure, being able to increase the restoration's longevity. This review aimed to evaluate the need for repair and suggest a standardized repair protocol to the main indirect restorative materials. For this, studies were surveyed from PubMed with no language or date restriction, to investigate the scientific evidence of indirect monolithic restoration repair with direct resin composite. A classification to guide clinical decisions was made based on the FDI World Dental Federation criteria about defective indirect restorations considering esthetic and functional standards, along with the patient's view, to decide when polishing, repairing or replacing a defective restoration. Based on 38 surveyed studies, different resin composite intraoral repair protocols, that included mechanical and chemical aspects, were defined depending on the substrate considering resin-based, glass-ceramic or zirconia restorations. The presented criteria and protocols were developed to guide the clinician's decision-making process regarding defective indirect monolithic restorations, prolonging longevity and increasing clinical success.

Repair of monolithic zirconia restorations with different direct resin composites: effect on the fatigue bonding and mechanical performance.

OBJECTIVE: The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites. MATERIALS AND METHODS: Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis. RESULTS: The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups. CONCLUSION: The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material. CLINICAL RELEVANCE: The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.

Conventional-, bulk-fill- or flowable-resin composites as prosthetic core build-up: Influence on the load-bearing capacity under fatigue of bonded leucite-reinforced glass-ceramic.

This study aimed to evaluate the fatigue performance of simplified ceramic restorations (leucite-reinforced glass ceramic) adhesively cemented onto substrates of different resin composites. Three options from the same commercial line were selected (Tetric N-Line, Ivoclar), classified as Conventional (CRC), Bulk-fill (BRC) and Flowable (FRC), which were used to make discs using a cylindrical metallic device (n = 19; Ø = 10 mm, thickness = 2.0 mm). A total of 57 discs (Ø = 10 mm, thickness = 1.0 mm) were made from CAD/CAM prefabricated blocks of a leucite reinforced glass-ceramic (Empress CAD, Ivoclar) to simulate a monolithic restoration, then were randomly distributed to be bonded on 19 discs of each three different resin composite substrates (CRC; BRC; or FRC) with a dual resin cement (Multilink N; Ivoclar). The samples were subjected to a compression test with a hemispherical stainless-steel piston (Ø = 40 mm) at a monotonic regimen (n = 4; 1 mm/min loading rate and 500 kgf loading cell until fracture). The cyclic fatigue test was performed underwater at a frequency of 20 Hz (n = 15). The first step was applied using 200N for 5000 cycles, followed by increments of 50N at each step of 10,000 until failure. The outcome considered for both tests was the occurrence of radial crack. Specific statistical tests (α = 0.05) were performed for monotonic (One-way ANOVA; Tukey's test) and fatigue data (Kaplan-Meier test; Log-rank test). Fractography of fractured samples were also performed. The FRC group had the lowest failure load in both test regimes (p < 0.05; monotonic: 726.64N; fatigue: 716.67N). There were no differences between the CRC and BRC groups (p > 0.05; monotonic: 989.30 and 990.11N; fatigue: 810.00 and 833.33N, respectively). The same result was obtained considering cycles for fatigue failure (FRC < CRC=BRC). Leucite glass-ceramic bonded to substrates made of flowable resin composite behaves worse mechanically than bonding to conventional or bulk-fill resin composite substrates.

Impact of try-in paste removal on the fatigue behavior of bonded lithium disilicate ceramics.

This in vitro study assessed the effectiveness of three cleaning protocols (air-water spray, 37% phosphoric acid, or Ivoclean) on lithium disilicate restorations' fatigue behavior after try-in paste application, compared to a clean condition. Lithium disilicate discs (IPS e.max CAD, Ivoclar) with Ø-= 12 mm and 1 mm thickness were prepared from prefabricated CAD-CAM blocks, polished, subjected to CAD-CAM milling topography simulation and crystallization. After, etching with 5% hydrofluoric acid and the application of try-in paste (Variolink try-in paste shade white; load of 2.5 N for 5 min) was performed. Discs that received try-in paste were divided into three groups according to the removal protocol: SPRAY - air-water spray for 30 s; HPO - active application of 37% phosphoric acid for 60 s; IVOC - application of Ivoclean for 20 s. Control group (CTRL group) did not receive the try-in paste application. Half of the specimens (n= 15) were tested in the baseline condition (24 h up to 7 days), and the others underwent 25,000 thermal cycles (5 - 55 °C) + 210 days of distilled water storage (37 °C). Additional specimens (n= 3) underwent monotonic testing (1 mm/min). Fatigue testing involved a cyclic fatigue approach (20 Hz, initial load = 100 N - 5000 cycles, step size = 50 N - 10,000 cycles) until a visible crack appeared. Fractographic and topographic analyses were performed. Fatigue data were statistically analyzed with two-way ANOVA, Kaplan-Meier log-rank (Mantel-Cox), and independent t-test (α= 0.05). In the baseline condition, the IVOC group resulted in a superior fatigue behavior compared to the CTRL and SPRAY groups, but similar to the HPO group. The HPO and SPRAY presented a similar fatigue behavior to the CTRL group. It was noticed a decrease in fatigue behavior after aging, which resulted in all the cleaning protocols leading to similar fatigue behavior compared to the CTRL group. On the SPRAY group surface, try-in pastes remnants were noticed. In summary, despite a detrimental impact at baseline conditions, all tested cleaning protocols seem proper to remove the try-in paste from the ceramic's surface in the long-term evaluation.

Cyclic fatigue of a repaired 4 YSZ ceramic: Effect of the repair protocol on the adhesive and mechanical behavior.

Objective: To evaluate the effect of different surface treatments on the morphology, shear bond, and flexural fatigue strength of a repaired translucent zirconia. Methods: Monolithic disc-shaped specimens of translucent zirconia were prepared and ground to simulate repair areas. Four groups underwent different treatments: Air-MDP (air-abrasion with alumina particles and 10-MDP primer), Si-Sil (silica-coated alumina particles with MDP-containing silane), Si-MDP (silica coating with 10-MDP primer), and Uni adhe (universal adhesive). After roughness measurements and treatments, repairs were done using resin composite. Shear bond and flexural (n = 15) fatigue tests were performed. Surface topography, interfacial analysis, fractographic, and finite element analysis were conducted. Results: The zirconia roughness was similar between the groups, however, the surface topography was modified according to the surface treatments. Si-Sil generated higher and more stable bond strength values (20.69 MPa) between translucent zirconia and resin composite when compared to Uni adhe (15.75 MPa) considering the fatigue bond strength scenario, while it was similar to Si-MDP (17.70 MPa) and Air-MDP (18.97 MPa). Regarding the mechanical behavior, Si-Sil (680.83 MPa) also showed higher and significantly different fatigue strength when compared to Uni adhe (584.55 MPa), while both were similar to Si-MDP (634.22 MPa) and Air-MDP (641.86 MPa). Conclusion: The association of mechanical and chemical approaches is essential for long-term bond strength and optimized mechanical behavior, being air-abrasion protocols and the use of silane and/or MDP-based primers suitable for zirconia repair protocols. It was found that relying solely on a universal adhesive was not as effective as other options available. Clinical significance: The surface treatment of repair protocols affects translucent zirconia's morphology. To enhance fatigue behavior in repaired monolithic zirconia, air abrasion is crucial. Exclusive use of a universal adhesive is less effective than other choices. A primer containing silane/MDP holds the potential for stable bond strength and optimized mechanical performance.

Effect of Surface Treatment and Resin Cement on the Bond Strength of an Advanced Lithium Disilicate.

OBJECTIVES: The aim of the study was to evaluate the effect of surface treatment and resin cement on the bond strength of conventional and advanced lithium disilicates (ALDs). MATERIALS AND METHODS: Ceramic slices (2 × 13 × 15 mm) of conventional lithium disilicate (LD) (IPS e.max CAD) and ALD (CEREC Tessera) were sectioned, polished, and divided into 16 groups (n = 10) according to the factors: ceramic, surface treatment, and resin cement (Panavia V5 and Variolink Esthetic DC). Surface treatments consisted of hydrofluoric acid 4.9% etching for 20 seconds (Hf20) or 30 seconds (Hf30), self-etching ceramic primer (Se), and sandblasting (Sb). Then, a resin cement cylinder (Ø = 2.5 mm) was manufactured on each specimen's surface. The specimens were then submitted to a shear bond strength (SBS) test. Surface roughness was evaluated through a contact profilometer, and surface morphology was evaluated under scanning electron microscopy for qualitative analysis. STATISTICAL ANALYSIS: Two-way analysis of variance (ANOVA) was used to analyze the data of SBS and surface roughness. For bond strength, the effects of surface treatment, resin cement, and the interaction were analyzed for each ceramic. For roughness, analyzed factors include ceramic and surface treatment. RESULTS: ANOVA revealed that ceramic (p = 0.047) and surface treatment (p < 0.001) factors affected the bond strength, while the cements performed similarly. Both materials showed adequate bond strength (ALD 19.1 ± 7.7 MPa; LD 17.1 ± 7.9 MPa). Sb protocol showed the lowest mean value (9.6 ± 2.9 MPa) compared with Hf20 (22.0 ± 7.1 MPa), Hf30 (21.7 ± 7.4 MPa), and Se (19.3 ± 6.0 MPa). CONCLUSION: For both ceramics, the highest performance was obtained after applying Se and Hf20 or Hf30. Therefore, longer etching time is unnecessary. Sb protocol must be avoided.

Effect of printing layer orientation and polishing on the fatigue strength of 3D-printed dental zirconia.

OBJECTIVE: The aim of the study was to evaluate the influence of surface polishing and printing layer orientation on the fatigue behaviour of 3 mol% yttria-stabilized zirconia (3Y-TZP) by stereolithography (SLA) in comparison with subtractive manufacturing. MATERIALS AND METHODS: 60 experimental zirconia bar-shaped specimens were 3D-printed (P) via SLA, and 30 specimens were milled (M) from commercial zirconia block (Lava™ Frame, 3 M ESPE AG). All specimens had the same dimensions (1 mm × 1 mm x 12 mm) after sintering. The 3D-printed specimens were randomly divided according to printing orientations: parallel or perpendicular to the tensile surface in the fatigue test. The specimens were subsequently submitted to two surface finishing protocols (n = 15/gr): unpolished or polished. Their phase compositions were analysed by X-ray diffraction. The fatigue behaviour was evaluated by a stepwise approach. RESULTS: The milled and both 3D-printed groups showed similar phase compositions for the as-sintered condition. Considerable amounts of rhombohedral phase were detected after polishing. Milled unpolished samples presented significantly higher fatigue strength than 3D-printed unpolished samples. Polishing did not improve the fatigue strength for milled zirconia but was advantageous for the 3D-printed specimens. 3D-printed specimens with parallel printing-layer orientation were significantly stronger than specimens with perpendicular layers regardless of surface finishing. CONCLUSION: The manufacturing techniques had a significant influence on the fatigue strength of 3Y-TZP, but not on the phase compositions of the surface. The polishing protocol showed different effects on 3Y-TZP fatigue strength and induced phase transition of the 3Y-TZP from Tetragonal to Rhombohedral. The best fatigue strength was achieved through milling using an unpolished surface and SLA-printed layers that were parallel to the tensile surface, followed by polishing.

Effect of abutment screw-access hole on the fatigue performance of implant-supported lithium-disilicate luted simplified restorations.

The present study aimed to evaluate the impact of the existence of an abutment screw-access hole and the filling effects on the fatigue mechanical behavior of a luted lithium-disilicate glass-ceramic. Seventy-two discs (Ø = 10 mm, 1.0 mm in thickness) of lithium disilicate (IPS e.max CAD, Ivoclar AG) were obtained from prefabricated blocks. Thirty-six abutment specimens of an opaque zirconia (Yz - IPS e.max ZirCAD, Ivoclar AG) and titanium (Ti - Luminesse Ti-Cam discs, Talladium Inc.) were confectioned, and allocated according to 6 groups: Yz and Ti rigid (without screw access hole); Yz unfilled, Yz filled, Ti unfilled and Ti filled (with the screw access (Ø = 2.5 mm) in the center). For the unfilled groups, only a polytetrafluoroethylene tape was used. Resin composite (Tetric N-Ceram, Ivoclar AG) was applied to the screw access hole for the filled groups (Yz and Ti). A cyclic fatigue test was carried out (load of 200 N, 10,000 cycles each; 20 Hz of frequency, step size of 100 N until failure detection (radial/cone crack). The fatigue failure load (FFL) and number of cycles until failure (CFF) were recorded for statistical purposes. The stress distribution (MPa) was evaluated by finite element analysis. A statistically positive effect of the abutment material and the presence of the screw access hole was observed (p ≤ 0.05). The rigid groups (without screw access holes) depicted almost 100% of survival after the fatigue tests. Among the other groups, the Yz-filled group showed the best performance (p ≤ 0.05), followed by the Yz unfilled group. The Ti groups depicted lower values of FFL and CFF, with the Ti unfilled group showing the most unfavorable fatigue behavior (p ≤ 0.05). The lowest tensile stress concentration in the restorative material was observed with the use of rigid abutments, the filled groups depicted intermediate values, while unfilled groups showed the highest stress concentration (Yz rigid = 306.3 MPa; Ti rigid = 310.4 MPa < Yz filled = 490.7 MPa; Ti filled = 498.9 MPa < Yz unfilled = 707.6 MPa; Ti unfilled = 719.7 MPa). Therefore, the presence of a screw-access hole decreases the mechanical performance of a lithium disilicate ceramic regardless of the abutment material. In the presence of a screw-access hole, zirconia abutments depicted a higher fatigue failure load when compared with titanium. The filling of the abutment screw-access hole with resin composite increased the mechanical performance of the simulated restoration.

Physical analysis of an acrylic resin modified by metal and ceramic nanoparticles.

BACKGROUND: Nanoparticles (NPs) have gained significant attention in various fields due to their unique properties and potential applications. Polymethyl methacrylate (PMMA) is an acrylic resin widely used in dentistry and medicine. However, the effect of different types of NP fillers on the physical properties of PMMA-based resins has not been thoroughly explored in the literature. OBJECTIVES: The present study aimed to evaluate the effects of 3 different types of NP fillers on the physical properties of an experimental PMMA-based resin as a function of the NP content and concentration. MATERIAL AND METHODS: Ten groups (n = 10) were designed. The specimens were composed of an acrylic resin, silicon dioxide (SiO2), cerium dioxide (CeO2), and titanium dioxide (TiO2) at the following ratios (wt%): group 1 (G1) - control; group 2 (G2) - 0.5% SiO2; group 3 (G3) - 1% SiO2; group 4 (G4) - 3% SiO2; group 5 (G5) - 0.5% CeO2; group 6 (G6) - 1% CeO2; group 7 (G7) - 3% CeO2; group 8 (G8) - 0.5% TiO2; group 9 (G9) - 1% TiO2; and group 10 (G10) - 3% TiO2. Transmission electron microscopy (TEM) was used to assess the quality of NP dispersion. Thermal stability was assessed with thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The effects of the abovementioned NPs on the properties of the resin were evaluated using the Archimedes principle for density, the Vickers hardness (VH) test and the impact strength (IS) test. Data analysis employed the oneand two-way analysis of variance (ANOVA), followed by Duncan's post hoc test at a significance level of 0.05. RESULTS: Transmission electron microscopy showed partial NP dispersion. All types of NPs enhanced the mechanical properties of the acrylic resin except for IS, which was similar to that of the control group. Among the types of NPs, irrespective of the weight percentage, CeO2 showed higher thermal stability and higher IS for 0.5 wt% and 1 wt% as compared to other groups, as well as the highest values of density at 0.5 wt%, 1 wt% and 3 wt%. Titanium oxide at 1 wt% presented a higher VH as compared to other groups. The fracture pattern was the same for all groups. CONCLUSIONS: Incorporating the tested NPs into the acrylic resin resulted in enhanced physical properties, primarily attributed to a lower NP content.

Mechanical Behavior of Repaired Monolithic Crowns: A 3D Finite Element Analysis.

This study evaluated the mechanical behavior and risk of failure of three CAD-CAM crowns repaired with different resin composites through a three-dimensional (3D) finite element analysis. Three-dimensional models of different cusp-repaired (conventional nanohybrid, bulk-fill, and flowable resin composites) crowns made of zirconia, lithium disilicate, and CAD-CAM resin composite were designed, fixed at the cervical level, and loaded in 100 N at the working cusps, including the repaired one. The models were analyzed to determine the Maximum Principal and Maximum Shear stresses (MPa). Complementary, an in vitro shear bond strength test (n = 10) was performed to calculate the risk of failure for each experimental group. The stress distribution among the models was similar when considering the same restorative material. The crown material affected the stress concentration, which was higher for the ceramic models (±9 MPa for shear stress; ±3 MPa for tensile stress) than for the CAD-CAM composite (±7 MPa for shear stress; ±2 MPa for tensile stress). The shear bond strength was higher for the repaired CAD-CAM resin composite (±17 MPa) when compared to the ceramics (below 12 MPa for all groups), while the repair materials showed similar behavior for each substrate. The stress distribution is more homogenous for repaired resin composite crowns, and a flowable direct resin composite seems suitable to repair ceramic crowns with less risk of failure.

Effect of Finishing Protocols on the Surface Roughness and Fatigue Strength of a High-Translucent Zirconia.

Purpose: In case of need for esthetical improvement of zirconia restorations, an individualization using extrinsic staining can be applied. This study aimed to evaluate the surface roughness and fatigue strength (survival) of high-translucency zirconia (3Y-TZP, YZ®HT, Vita Zanhfabrik) with extrinsic characterization and/or glaze. Methods: Sixty (60) zirconia discs (12 × 1.2 mm) were obtained, sintered, and randomly distributed among three groups (n = 20) according to the surface finishing protocol: C (control), C + G (extrinsic characterization followed by a glaze layer), and G (glaze layer). The surface roughness (Ra) was analyzed with a contact profilometer. Subsequently, the specimens were subjected to a fatigue load profile starting at 120 N during 20,000 cycles at 4 Hz frequency, with a 5% increase at each step until failure. The failed specimens were evaluated under a stereomicroscope. Surface roughness analysis was evaluated by using one-way ANOVA and post hoc Tukey tests (95%); while fatigue survival probability was analyzed with Kaplan-Meier and Mantel-Cox (log- rank, 95%). Results: One-way ANOVA revealed that surface roughness was affected by the finishing protocol, where C + G showed the highest mean value (0.46 ± 0.18 µm)A followed by G (0.30 ± 0.10 µm)B, and C (0.19 ± 0.02 µm)C. While for fatigue strength, the G protocol presented a higher mean value (243.00, and 222.36-263.63)A, followed by C + G (192.75 and 186.61-198.88)B and C (172.50 and 159.43-185.56)C. Conclusion: Surface finishing protocols modify the surface roughness and fatigue strength of high-translucent zirconia. Regardless of the surface roughness, both glazing protocols improved the ceramic fatigue strength, favoring the restoration's long-term survival.

The loss of resin cement adhesion to ceramic influences the fatigue behavior of bonded lithium disilicate restorations.

When partial and/or non-retentive preparation, such as those for occlusal veneers, is indicated, a proper and stable adhesion is essential. Therefore, the aim of this in vitro study was to evaluate the effect of loss of adhesion in different regions of the bonding interface on the fatigue behavior of simplified lithium disilicate restorations. For this, lithium disilicate (IPS e.max CAD) discs (1 mm thick and Ø = 10 mm) were fabricated, polished with #400-, #600-, #1200-grit silicon carbide (SiC) papers, and crystallized. As substrate, fiber-reinforced resin epoxy discs (2.5 mm thick and Ø = 10 mm) were fabricated and polished with #600-grit SiC paper. The ceramic bonding surface was treated with 5% hydrofluoric acid and a silane-containing primer (Monobond N), while the substrate was etched with 10% hydrofluoric acid followed by the application of the bonding system primers (Primer A + B). A lacquer (nail polish) was used to simulate the loss of adhesion in specific areas according to the study design to compose the testing groups: bonded (control; did not received nail polish application); - non-bonded (loss of adhesion in the whole specimen area); - margin (loss of adhesion in the ceramic margin); - center (loss of adhesion in the ceramic central area). The adhesive area of partially bonded groups was 50% of the adhesive surface. Then, the discs (n = 12) were bonded to the respective substrate using a resin cement (Multilink N), light-cured, water-stored for 90 days, and subjected to thermocycling (25,000 cycles, 5° to 55 °C) before testing. A cyclic fatigue test was run (20 Hz, initial load of 200 N for 5000 cycles, 50 N step size for 10,000 cycles each until specimen failure), and the fatigue failure load and number of cycles for failure were recorded. As complementary analysis, finite element analysis (FEA) and scanning electron microscopy analysis were performed. Kaplan-Meier log-rank (Mantel-Cox) was conducted for survival analysis. The results showed that as the loss of adhesion reaches the central area, the worse is the fatigue behavior and the higher is the stress peak concentration in the ceramic bonding surface. The bonded specimens presented better fatigue behavior and stress distribution compared to the others. In conclusion in a non-retentive preparation situation, proper adhesion is a must for the restoration fatigue behavior even after aging; while the loss of adhesion reaches central areas the mechanical functioning is compromised.

Does glaze firing affect the strength of advanced lithium disilicate after simulated defects?

OBJECTIVE: To study the influence of glazing on strength repair of lithium disilicate glass-ceramics after defect incorporation in different production processing phases. MATERIALS AND METHODS: Bar-shaped specimens (1 × 1 × 12 mm, n = 280; 20/group) made from different lithium disilicate ceramics (IPS e.max CAD, Ivoclar, "LD" or advanced lithium disilicate CEREC Tessera, Dentsply Sirona, "ALD") were exposed to 7 different protocols: crystallized without (c) and with glaze layer (cg), with a defect incorporated before crystallization without (ic) and with glaze layer (icg), with a defect after crystallization without (ci) or with glaze layer (cig), and defect incorporated after the glaze layer (cgi). The flexural strength was determined using the three-point bending test. Analysis of indented areas and fractured specimens was performed by scanning electron microscopy. Flexural strength data were evaluated by two-way ANOVA followed by Tukey tests (α = 5%). RESULTS: Two-way ANOVA revealed a significant influence of ceramic (p < 0.001; F = 55.45), protocol (p < 0.001; F = 56.94), and the interaction protocol*ceramic (p < 0.001; F = 13.86). Regardless of ceramics, defect incorporation as final step resulted in the worst strength, while defects introduced before crystallization did not reduce strength. Glaze firing after defect incorporation led to strength repair for ALD, whereas such an effect was not evident for LD. CONCLUSIONS: The advanced lithium disilicate must receive a glaze layer to achieve its highest strength. Defects incorporated in the pre-crystallized stage can be healed during crystallization. Defects should not be incorporated after glazing. CLINICAL RELEVANCE: Clinical adjustments should be performed on pre-crystallized or crystalized restorations that receive a glazer layer afterwards.

Post-fatigue fracture load, stress concentration and mechanical properties of feldspathic, leucite- and lithium disilicate-reinforced glass ceramics.

Objective: To evaluate the mechanical properties of different CAD/CAM ceramic systems and the post-fatigue fracture and stress distribution when used as cemented crowns. Materials and methods: Sixty (60) CAD/CAM monolithic crowns were milled using three different ceramic materials (FD - Feldspathic [Vita Mark II]), LE - Leucite-based ceramic [IPS Empress CAD] and LD - Lithium Disilicate [IPS e.max CAD]) and adhesively cemented on resin composite dyes. Specimens were stored in distillated water (37 °C) for 7 days. After, half of the crowns were submitted to immediate fracture load test while the other half was submitted to fatigue cycling. The average cement layer of approximately 80 µm was assessed using scanning electron microscopy (SEM). The average thickness was used in the three-dimensional (3D) Finite Element Analysis (FEA). For each ceramic material, the density, Poisson ratio, shear modulus, Young modulus, fracture toughness, and true hardness were assessed (n = 3). The data was used to assess the Maximum Principal Stress throughout 3D-FEA according to each material during load to fail and post-fatigue. Data were submitted to two-way ANOVA and Tukey test (α = 0.05). Results: LD showed the highest compression load, density, shear modulus, Young modulus, fracture toughness and true hardness values. While LE presented the lowest mechanical properties values. There is no difference in the Poisson ratio between the evaluated ceramics. Conclusion: LD was susceptible to aging process but presented stronger physicomechanical properties, showing the highest post-fatigue fracture load and highest stress magnitude.